thermoplastic low smoke halogen-free flame retardant polyolefin compound jacket material thermoplastic low smoke halogen-free flame retardant polyolefin compound jacket material thermoplastic low smoke halogen-free flame retardant polyolefin compound jacket material thermoplastic low smoke halogen-free flame retardant polyolefin compound jacket material
Next

thermoplastic low smoke halogen-free flame retardant polyolefin compound jacket material

1.1 ~ 1.6 / Kilogram

|

1000 Kilogram Minimum Order

País:

China

N º de Modelo:

SHD 01-H-02

Precio FOB:

1.1 ~ 1.6 / Kilogram Obtener el precio más reciente

Lugar de origen:

Yuanshi country, Hebei Province, China

Precio de pedido mínimo:

1.1 per Kilogram

Cantidad de pedido mínimo:

1000 Kilogram

Detalle de embalaje:

Packing: N. W: 25kg/1000kg bags with inner bag of aluminum -plastic composite vacuum

El tiempo de entrega:

7-15 days

Capacidad de suministro:

10000000 Kilogram per Week

Tipo de pago:

T/T

Contactar ahora
Miembro Básico

Persona de contacto Tina

Shijiazhuang, Hebei

Contactar ahora

Especificaciones del producto

  • Density:1.45g/cm3
  • Hardness (Shore D):58
  • Tensile strength:12.5Mpa
  • Elongation at break:215%
  • Tensile strength after aging:11.3Mpa
  • Rate of change in tensile strength:+15

Descripción del producto

Sell cable compound material
Thermoplastic low smoke halogen-free flame retardant polyolefin compound jacket material

Standard: GB/T*********5, IEC*************9
1. The product not only has excellent low-smoke halogen-free flame retardant performance,but also has excellent extrusiion processing performance. It can be extruded on an ordinary PVC extruder. As long as the cooling device is normal, the extrusion processing speed can be accelerated. The performance of thid product is batter than similar products.

  The series are based on polyolefin and contain special halogen-free flame retardants and smoke suppresants,which are processed by precise mixing with special formulas. When the cable structure is desugned reasonably, it can pass the A/B/C type combustion test and meet the light transmittance requirments. When burning, no halogen acid gas is released, the amound of toxic and crossive gas is vey small and the smokeconcentration is very low. We can also provide anti-termite, anti-rodent and UV resistant properties according to customer requirment.

2.Feature ans uses
This product is suitable for accasions with high flame retardant requirments and low secondary hazards, such as subways, ships, high-rise building program-controlled switch rooms, computer rooms and various crowded public places. Suitabke for optical cable and wire core working termperature *0℃ low smoke halogen free flame retardant cable sheath. This product is guaranteed to pass verious beam burning tests and light transmittance tests. What's more, it has super cracking resistance property.

3. Extrusion process
The drying temperature is *5℃ and the drying time is at least 2 hours. It is advisable for the hot material to enter the extruder. It can be extruded by L/D ****5 extruder. When the screw compression ratio is low, the output volume is large. Ecah zone of the extruder must have a cooling control system and the indicated value of the temperaturecontrol table varis with the typr of extruder, each user should select a suitable temperature according to the specific conditions of the extruder used. The following temperatures can be used as a referancefor commissioning:
The following temperatures can be used as a reference for commissioning:

Barrel position Zone 1 Zone 2 Zone 3 Zone 4 nose and mode
temperature(℃) **5±5 **5±5 **5±5 **5±5        **0±5
The machine head can be withour a filter screen or a filter screen below *0 mesh can be used. It can be matched with special color masterbatch, the dosage is about **2%, generally does not affect the materials properties
Note: If the aluminum-plastic composite inner bag's damp proof fails, it should be dried before use. The drying temperature should be *5℃ ad the drying time should be at least 2 hours. It is better for hot material to enter and leave the extruder.
4. Packaging, transportation and storage:
Packing: N. W: *5kg/***0kg bags with inner bag of aluminum -plastic composite vacuum moisture-proof bag and outer packing being made of kraft paper composite bag or woven bag. It should not be exposed to the sun and the rain during transport. It should be stored in a clean, cool, dry and ventilated warehouse. It should be handled with care.
5. Shelf life: 6 months

País: China
N º de Modelo: SHD 01-H-02
Precio FOB: 1.1 ~ 1.6 / Kilogram Obtener el precio más reciente
Lugar de origen: Yuanshi country, Hebei Province, China
Precio de pedido mínimo: 1.1 per Kilogram
Cantidad de pedido mínimo: 1000 Kilogram
Detalle de embalaje: Packing: N. W: 25kg/1000kg bags with inner bag of aluminum -plastic composite vacuum
El tiempo de entrega: 7-15 days
Capacidad de suministro: 10000000 Kilogram per Week
Tipo de pago: T/T
Grupo de productos : thermoplastic LSZH cable material