China manufacture Irradiation cross-linked LSZH flame retardant polyolefin insulation compound

Precio FOB

Obtener el precio más reciente

( Negotiable )

1000 Kilogram Minimum Order

País:

China

N º de Modelo:

SHFD02-05j-01

Precio FOB:

( Negotiable )(Negociable) Obtener el precio más reciente

Lugar de origen:

Yuanshi Country, Hebei Province, China

Precio de pedido mínimo:

Cantidad de pedido mínimo:

1000 Kilogram

Detalle de embalaje:

N.W: 25kg bags with inner bag of plastic film moisture-proof bag and outer packing being made of kra

El tiempo de entrega:

7-15 days

Capacidad de suministro:

1000000 Kilogram per Week

Tipo de pago:

T/T

Grupo de productos :

irradiation cross-linked cable compound

Contactar ahora

Hebei Sunua Advanced Material Co., ltd

China

Miembro Básico

Persona de contacto Tina

Shijiazhuang, Hebei

Contactar ahora

Especificaciones del producto

Density :1.45g/cm3
Tensile strength :13Mpa
Elongation at break :189%
Oxy index :36
Toxicity index:0.4

Descripción del producto

Irradiation cross-linked LSZH flame retardant polyolefin insulation compound

This series of products have good processing performance, physical and mechanical properties, insulation properties and excellent flame retardant properties, do not release halogen acid, self-extinguishing when away from fire, can greatly reduce the emission of toxic and corrosive gases and the generation of smoke, fully complies with the requirements of EU RoHS directive and REACH directive.

MODEL : SHFD**-05J**1/SHFD****5J**1

The series is a cross-linked low-smoke halogen-free flame retardant polyolefin material independently developed and produced by our company. It is processed by mixing and granulating. It has good extrusion processing performance and excellent stability. It is suitable for low-smoke and halogen-free control of temperature resistance of **5°C/**5°C. Cables, automotive cables, instrumentation cables and other fields.

1. Implement the standard: GB/T*********5
2. Features and uses
It has the best cost performance and excellent extrusion performance. It can be widely used in control cables, power cables, instrument cables, electronic wires and other fields. Such as: subways, ships, power stations, high-rise buildings, program-controlled switch rooms, computer rooms and various crowded public places.
3. Extrusion process
This product has the same (or similar) extrusion process as the low-smoke halogen-free flame retardant polyolefin cable material:

barrel position	zone 1	zone 2	zone 3	zone 4	nose and mode
Temperature(â„ƒ)	135±*0	145±*0	155±*0	1*0±15	*65±15

Note: Due to the different processing equipment, the plasticizing ability of the material is different, so in the initial production trial process, the temperature is only for reference, and the production speed is about *0% of the normal production speed for trial production.

4. Packaging, transportation and storage
Packing: N.W: *5kg bags with inner bag of plastic film moisture-proof bag and outer packing being made of kraft paper composite bag .
Transportation and storage: It should not be exposed to the sun and rain during transport. It should be stored in a clean, cool, dry and ventilated warehouse. It should be handled with care.
5. Shelf life : 6 months
6. Physical and mechanical properties

Project name		Units	Test Method	Typical Value
Project name		Units	Test Method	SHFD-05J1	SHFD5J1**
Density		g/cm³	GB/T ***3.1	1.*4	1.*5
Tensile strength		MPa	GB/T ***0.3	3.2	2.6
Elongation at break		%	GB/T ***0.3	**0	**9
Heat extension test ï¼ˆ*0â„ƒ 5min 0.2MPaï¼‰	Max Elongation under load	%	GB/T **1.1	*4	*0
Heat extension test ï¼ˆ*0â„ƒ 5min 0.2MPaï¼‰	Permanent elongation after cool	%	GB/T **1.1	2	3.5
Heat ageing testï¼ˆ6/8â„ƒ×**8hï¼‰	Rate of change in tensile strength	%	GB/T **1.1	8	*2.3
Heat ageing testï¼ˆ6/8â„ƒ×**8hï¼‰	Change rate of elongation at break	%	GB/T **1.1	*4	*6.8
Low temperature impact embrittlement temperature(**5â„ƒ)		Number of failures	GB/T ***0	pass	pass
Dielectric strength at *0â„ƒ		MV/m	GB/T ***8.1	*9	*5
Volume resistivity at *0â„ƒ		Ω.m	GB/T ***0	3.0×0^2	3.7×0^*2
Water immersion test 0â„ƒ *8hr	Rate of change in tensile strength	%	GB/T ****9	*8	*9
Water immersion test 0â„ƒ *8hr	Change rate of elongation at break	%	GB/T ****9	6	5
Smoke density( flaming)			GB/T ***3.2	*2	*5
Smoke density(no			GB/T ***3.2

País:	China
N º de Modelo:	SHFD02-05j-01
Precio FOB:	( Negotiable ) (Negociable) Obtener el precio más reciente
Lugar de origen:	Yuanshi Country, Hebei Province, China
Precio de pedido mínimo:	-
Cantidad de pedido mínimo:	1000 Kilogram
Detalle de embalaje:	N.W: 25kg bags with inner bag of plastic film moisture-proof bag and outer packing being made of kra
El tiempo de entrega:	7-15 days
Capacidad de suministro:	1000000 Kilogram per Week
Tipo de pago:	T/T
Grupo de productos :	irradiation cross-linked cable compound