Sell Specific floating agent

Description

I. Basic performance and application
Compared with traditional floating agent, T**8 specific floating agent enjoys better concentration effect to change the ordinary flat powder to wrinkle powder with strongspatial effect. Particularly, it is very applicable to large textured powder, such as black background gold flower, black background silver flower or the like and the effect is good unexpectedly. It is of smaller pollution compared with spatial texturing agent and poorer compatibility and heavier pollution compared with ordinary floating agent.
 
II. Technical indexes
Appearance: white powder
Fineness:                                                                   ******0 mesh
Volatile content:                                                         ≤0.5%
 
III. Basic ingredients of powder coating (large texture black background silver flower) (dose: 0.5~1% outer mixing)
Name                                                                           Weight
Epoxy resin (E**2)                                                       **0
Polyester resin (5: 5)                                                   **0
Precipitated barium sulfate                                           **0
T**0 Antistatic agents                                                 5
TA**0 silver powder brightening agent                       5
MA***0 carbon black                                                   7
T**2 high light wax                                                      5
Base powder **0g + 0.5g T**8 specific floating agent + 0.8g T**8 silver powder
 
IV. Coating manufacturing technology:
Extruder: double screw extruder
Extruder prezone temperature:                                  **5º
Extruder postzone temperature:                                **0º
Extruder speed:                                                         *0HZ
 
V. Baking temperature: **0º/*5min or **0º/*0min
Basic performance of coating film: film thickness of *0~**0μm
Impact strength (positive and negative):                     *0kg/cm passed
Pencil hardness:                                                          ≥2H
glossiness (*0º angle):                                               ≥*0º
Bending (Φ2um):