Sell surfactant

Description

I. Basic performance and application
T**6 surfactant can increase the coat levelness and compactness, relieve orange peel, eliminate pinhole, obviously enhance the plate surface smoothness, remove the coat surface mist, greatly increase the brightness and effectively improve the coat film surface glossiness. T**6, as a surface active substance, can be applicable to the production of various thermoset powders.
 
II. Technical indexes
Appearance: white micronized powder
Melting point:                                                             **5~**5℃
Volatile content:                                                         0.2%
 
III. Basic ingredients of powder coating (full gloss, white powder) (dose: 0.5% inner extruding)
Name                                                                           Weight
Epoxy resin (E**2)                                                       **0
Polyester resin (5: 5)                                                   **0
Titanium pigment (rutile)                                              **0
Precipitated barium sulfate                                           **0
T*8 pure leveling agent                                               *0
T**1 luster-enhancing agent                                       *0
Yellow stain resistant benzoin                                      5
T**6 surfactant                                                           5
T**2 high light wax                                                      5
 
IV. Coating manufacturing technology:
Extruder: double screw extruder
Extruder prezone temperature:                                  **5º
Extruder postzone temperature:                                **0º
Extruder speed:                                                         *0HZ
 
V. Baking temperature: **0º/*5min or **0º/*0min
Basic performance of coating film: film thickness of *0~*0μm
Impact strength (positive and negative):                     *0kg/cm passed
Pencil hardness:                                                        ≥1.5H
glossiness (*0º angle):                                               ≥*0º
Bending (Φ2um):      passed