Water-base Microlayer Corrosion Protection Coating JH-9390 By Changzhou Junhe Technology Stock., LTD,

Water-base Microlayer Corrosion Protection Coating JH-9390

Precio FOB

Obtener el precio más reciente

( Negotiable )

40 Kilogram Minimum Order

País:

China

N º de Modelo:

JH-9390

Precio FOB:

( Negotiable )(Negociable) Obtener el precio más reciente

Lugar de origen:

CHINA

Precio de pedido mínimo:

Cantidad de pedido mínimo:

40 Kilogram

Detalle de embalaje:

Pack A:16kg/ Metal Barrel Pack B:24KG Plastic Barrel

El tiempo de entrega:

Ten days after receipt of advance payment

Capacidad de suministro:

2 Ton per Day

Tipo de pago:

Other, L/C, T/T

Grupo de productos :

Especificaciones del producto

Other Names: zinc flake coating paint
Purity (%): 90%
Classification: Specific Reagents
Brand Name: JUNHE

color:silver
Specific gravity:1.30Ã‚Â±0.05
Viscosity::20~60s(Spray Coating) 60~90S(Dip-Spin Coating)
ph:3.8-5.2

Descripción del producto

Product Details:

Brand Name: JUNHE

Model Number: JH****0

Minimum Order Quantity: **0 Kilograms

Packaging Details: Pack A:*6kg/ Metal Barrel

Pack B:*4KG Plastic Barrel

Pack C:Based on the amount of B agent A

Delivery Time: Ten days after receipt of advance payment

Supply Ability: 2 Tons per Day

Coating Method: Dip Spin & Spray

PH: 3.**5.2

Viscosity: *0~*0s(Spray Coating) *0~*0S(Dip-Spin Coating)

Color: Silver

Specific Gravity: 1.*0±0.*5

Operating Temperature: *0±2â„ƒ

JH****0 is made up of three packs: A,B and C;

Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and ethylene glycol. The radius-thickness ratio of Zn plate is *0~**0.

Pack B: It is the solvent of the coating colored in orange-red and in water solution, which contain the Cr6+.

Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.

Coating Process:

1. Mix Ratio

Pack A:*6.0 kg

Pack B:*4.0 kg (the quantity can be increased appropriately if spray coating)

Pack C:***0 g (according to different viscosity demand )

2. Mixture Method

Before Mixture, Keep weighted A&B into the water bath at *5±2â„ƒ , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to *0r/min, and add B.

Add B to the stirring A slowly. At the moment, the barrel temperature will go up, when it reaches *5â„ƒ, startup refrigerating device to keep the barrel temperature constant at *5â„ƒ.

3. Stir the mixture about 1~2 hours fast after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than *0â„ƒ, otherwise C will not be dissolved sufficiently .)Then stir *2 hours continuously.

4. The coating should be filtrated by *0~**0 mesh stainless steel screen before pouring into dip barrel.

5. Temperature control device should be equipped with dip barrel to keep the temperature of coating at *2±2â„ƒ.

(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.

6. Test density, PH, Temperature, Viscosity and Cr6+ content of coating every 8 hours if operate continuously.

Technical data:

No.	Item	Data
1	Color	Silver
2	Coating method	Diping & Spraying
3	PH	3.**5.2
4	Specific gravity	1.0±0.5
5	Viscosity	0~0s(Spray Coating) 0~0S(Dip-Spin Coating)
6	Operating temperature	*0±2â„ƒ

País:	China
N º de Modelo:	JH-9390
Precio FOB:	( Negotiable ) (Negociable) Obtener el precio más reciente
Lugar de origen:	CHINA
Precio de pedido mínimo:	-
Cantidad de pedido mínimo:	40 Kilogram
Detalle de embalaje:	Pack A:16kg/ Metal Barrel Pack B:24KG Plastic Barrel
El tiempo de entrega:	Ten days after receipt of advance payment
Capacidad de suministro:	2 Ton per Day
Tipo de pago:	Other, L/C, T/T
Grupo de productos :	-