Precio FOB
Obtener el precio más reciente1100 ~ 1600 / Ton
|5 Ton Minimum Order
País:
China
N º de Modelo:
-
Precio FOB:
1100 ~ 1600 / Ton Obtener el precio más reciente
Lugar de origen:
-
Precio de pedido mínimo:
1100 per Ton
Cantidad de pedido mínimo:
5 Ton
Detalle de embalaje:
25kg/ingot, 1MT/bundle
El tiempo de entrega:
15 days after receive the depoist
Capacidad de suministro:
10000 Ton per Month
Tipo de pago:
T/T, L/C
Grupo de productos :
Persona de contacto Kimmy
Room 2608,Ginza jingdu international building,shizhong district, Jinan City, Shandong
Al% : 3.**4.2%
Zamak 5 propertiesPropertyMetric valueEnglish valueMechanical propertiesPhysical properties
Ultimate tensile strength | **1 MPa (**0 MPa aged) | *8,**0 psi (*9,**0 psi aged) |
Yield strength (0.2% offset) | **5 MPa | *3,**0 psi |
Impact strength | *2 J (*6 J aged) | *8 ft-lbf (*1 ft-lbf aged) |
Elongation at Fmax | 2% | |
Elongation at fracture | 3.6% (*3% aged) | |
Shear strength | **2 MPa | *8,**0 psi |
Compressive yield strength | **0 MPa | *7,**0 psi |
Fatigue strength (reverse bending 5x**8cycles) | *7 MPa | 8,**0 psi |
Hardness | **4 Brinell | |
Modulus of elasticity | *6 GPa | *4,**0,**0 psi |
Solidification range (melting range) | *****6 °C | *****7 °F |
Density | 6.7 kg/dm3 | 0.*4 lb/in3 |
Coefficient of thermal expansion | *7.4 μm/m-°C | *5.2 μin/in-°F |
Thermal conductivity | **9 W/mK | **6 BTU-in/hr-ft*-°F |
Electrical resistivity | 6.*4 μΩ-cm at *0 °C | 2.*7 μΩ-in at *8 °F |
Latent heat (heat of fusion) | **0 J/g | 4.7x***5 BTU/lb |
Specific heat capacity | **9 J/kg-°C | 0.**0 BTU/lb-°F |
Coefficient of friction | 0.*8 |
País: | China |
N º de Modelo: | - |
Precio FOB: | 1100 ~ 1600 / Ton Obtener el precio más reciente |
Lugar de origen: | - |
Precio de pedido mínimo: | 1100 per Ton |
Cantidad de pedido mínimo: | 5 Ton |
Detalle de embalaje: | 25kg/ingot, 1MT/bundle |
El tiempo de entrega: | 15 days after receive the depoist |
Capacidad de suministro: | 10000 Ton per Month |
Tipo de pago: | T/T, L/C |
Grupo de productos : | Zinc Ingot |