Descripción del producto

Introduction:

A nickel-chromium alloy with good oxidation resistance at higher temperatures. With good resistance in carburizing and chloride containing environments.

Alloy **0 is a nickel-chromium alloy designed for use from cryogenic to elevated temperatures in the range of ***0 deg F(***3 deg C). The high nickel content of the alloy enables it to retain considerable resistance under reducing conditions and makes it resistant to corrosion by a number of organic and inorganic compounds. The nickel content gives it excellent resistance to chloride-ion stress-corrosion cracking and also provides excellent resistance to alkaline solutions.

Its chromium content gives the alloy resistance to sulfur compounds and various oxidizing environments. The chromium content of the alloy makes it superior to commercially pure nickel under oxidizing conditions. In strong oxidizing solutions like hot, concentrated nitric acid, **0 has poor resistance. Alloy **0 is relatively un-attacked by the majority of neutral and alkaline salt solutions and is used in some caustic environments. The alloy resists steam and mixtures of steam, air and carbon dioxide.

Alloy **0 is non-magnetic, has excellent mechanical properties and a combination of high strength and good workability and is readily weldable. Alloy **0 exhibits cold forming characteristics normally associated with chromium-nickel stainless steels.

Typical corrosion applications include titanium dioxide production (chloride route), perchlorethylene syntheses, vinyl chloride monomer (VCM), and magnesium chloride. Alloy **0 is used in chemical and food processing, heat treating, phenol condensers, soap manufacture, vegetable and fatty acid vessels and many more。

Characteristics

• Resistant to a wide range of corrosive media. The chromium content gives better resistance than Alloy **0 and **1 under oxidizing conditions, at the same time the high nickel gives good resistance to reducing conditions.
• Virtually immune to chlorine ion stress corrosion cracking.
• Demonstrates adequate resistance to organic acids such as acetic, formic and stearic.
• Excellent resistance to high purity water used in primary and secondary circuits of pressurized nuclear reactors.
• Little or no attack occurs at room and elevated temperatures in dry gases, such as chlorine or hydrogen chloride. At temperatures up to **0C in these media, this alloy has been shown to be one of the most resistant of the common alloys.
• At elevated temperatures the annealed and solution annealed alloy shows good resistance to scaling and has high strength.
• The alloy also resists ammonia bearing atmospheres, as well as nitrogen and carburizing gases.
• Under alternating oxidizing and reducing conditions the alloy may suffer from selective oxidation

Specifications:

Bar: ASTM B**6    AMS***5    DIN****2

Plate/Sheet: ASTM B**8   AMS***0  DIN****0

Tube/pipe: ASTM B**7,  ASTM B**3

Fittings: ASTM B**6

Forgings: ASTM B**4, DIN****4

Weld Wire: FM *2/ENiCrFe*3

Weld Electrode:  FM**2/ ENiCrFe*3