mold gypsum resin silicone rubber

Descripción del producto

                                                                           Technical Date Sheet
                                                                      Tin-Cured Silicone Rubber

Description
5series is a kind of room temperature vulcanized silicone rubber in condensation type. Its generally named as two part silicone rubber , Part A is a flowable liquid, part B is the curing agent or catalyst . Its mainly used for mold making.

Application
5series silicone rubber is used for making molds of gypsum decoration, plaster ornaments,  polyester decoration, unsaturated resin crafts, poly-resin crafts, polyurethane, bronze, wax, candle, and similar products . 
 
5series Silicone rubber is a kind of soft silicone with good fluidity ,it is suitable for small size product with detailed pattern by pouring operation, especially popular for the manufacturer of very small resin crafts and candle decorations .

   ~Characteristics
＊An exceptional fluidity and good operability, easy to demold
＊A kind of soft silicone 
＊Good tensile strength and tear strength
＊Cure at room temperature 
＊Good flexibility 
＊Outstanding bubble releasing 
＊Good duplication times  
                                                            

                                                                Technical Date Sheet

                                                              Platinum Cured Silicone

Description
　addition cure silicone is a kind of two part silicone rubber in addition cure or platinum cure type with mixing ratio of 1:1.  It can cure at room temperature as well as under heat. It's a kind of food grade silicone and mainly used for mold making.
Application
　　　silicone rubber is mainly used for making molds of tire,concrete stone,GRC,polyurethane products; wax, candle decoration; rapid prototyping and tyre molds; chocolate, candy and similar products.

 Characteristics 
＊An exceptional fluidity and good operability, easy to demold
＊Good tensile and tear strength
＊Outstanding bubble releasing
＊Non-deformation
＊Low shirinkage
＊Aging resistance ,high temperature resistance (**0℃)
＊Environmentally, food-grade
Package
*0KG/drum vacuum packing for part A + *0KG/drum vacuum packing for part B
**0KG/drum packing for part A ***0KG/drum packing for part B

Operation instructions
Step 1: prepare the original molds
Make sure your original molds perfect. fix it on a board. And fix the original mold on a board , then used four piece of board to enclose the original molds .

 
Step 2: Take **0 G parts A and add 3G parts B and mix them evenly. 
Notes: Mold making silicon rubber is a kind of flowing liquid ,it contains two parts. Part A is a kind of flowing white liquid and part B is the curing agent or catalyst .Pls follow the step strictly:
         1.Weigh the two part exactly by electronic weight.. 
If not , for example add two much catalyst , the operation time will be too fast to operate ,which will cause inconvenience to operate . 
         2.Mix part A and part B evenly. 
Otherwise the silicon rubber will be partly solidified and this will give birth to difficulties in your final operation. Whats more, the finished molds will meet a short life. All of these will cause a waste of silicon rubber.

Step 3: Vacuum pumping
Without exception, this step takes less than *0 minutes. Otherwise, it will cause cross linking reaction, and no more further steps will be available. 
 
Step 4: Pouring casting or Brush operation
Notes:1. For simple pattern products we suggest use pouring operation way , which will be very easy to operate and demould. Pourable silicone require light viscosity which will be easy to flow smoothly and easy to de-air . 
        2.For delicate pattern products we suggest use brushing operation way , which can copy the pattern exactly . Brushable silicone require high viscosity which wont be easy to flow away and easy to brush .    3. We suggest to set the silicone mold for another *2 hours after demould before put into large production .