Descripción del producto

Good Heavy best quality ***********0m3 AAC Block Machine

 Introduction of AAC Block Machine

    AAC Brick Production Line (light brick ) is the light and porous buidling material. It has light weight keeping temperature cant burn and other advantages.it can be made into many kinds of bricks(for example:**0×**0×**0,*0×*0×**0,**0×**5×*3,**0×**0×**5),they could be used industry building and common building.they are more and more popular in the world.in the future,they will replace the Clay brick completely.

 AAC Block Machine

     Common concrete density is usually ****- ***0kg/m3,but AAC Machine are **0kg/m****0kg/m3

It has not the big grain,main use silicon material (for example:coal ash,sand,stone dust and others ),through making the material small for example sand,they can be used directly if has enough degree of small (for example coal ash.Mixing  calcium material lime cement water to a special slop,then add the aluminum dust and the additive.Make the aluminum dust and the special slop have a Chemical reflect.then produce Hydrogen to make the concrete slop to expanding or swell,foam.Next,put them into the curing room to concreting cutting steaming curing,last,there will bacome the light brick,the porous rate is ****0%.

 AAC Block Machine

     Equipments in the aac production line

 stocking raw materials, mixing, molding, forming, cutting, evaporating and curing, crane cramp, transporting etc.,

1        Product weight is according to **0kg/m3 to control.

2        annual capacity **0,**0M3.

3        set raw  material proportion: cement 6.5%, raw lime *3%, flyash *8%, gypsum 3%, aluminum paste powder **0g/M3.

4        water and material rate 0.**1

5        one mould product 2.*8M3

6        Casting slurry cycle time **6 minutes, cut cycle time 5 minutes.

7        casting slurry temperature ****2 degree

8        body quiet stop. Time is 1.**2.5hours, temperature **-       

           *0 degree, after quiet stop body strength is 0.***0.*8Mpa

9        Steam curing cycle time, come in and out autoclave about 0.5hour, steam curing cycle time about is 6 hours/1.6Mpa, total 6.5 hours.

*0. Cement lime fly ash style aerated block raw material proportion

*1.  Cement lime Sand style aerated block raw material proportion

Reference: cement is *2.5 Portland or *2.5 common cement

Aluminum power paste calculate to use according to **0kg/m3 
Remark: the accurate batching rate is adjustable according to the raw material locally