Descripción del producto

Yuwang YT*1 is a universal instant adhesive which hasthe ability of rapidly adhering to many base materials (including metal, plastic and rubber) and is also used to adheretoacid and porous materials such as wood, paper, leather and fabric.



Brand: Yuwang

Package size: *0**0**5cm

Technology: cyanoacrylate

Chemical type: ethyl cyanoacrylate

Appearance (uncured): colorless clear liquid

Composition: single component

Viscosity: low

Curing method: moisture cured

Application: adhesion

Main adhesive materials: metal, plastic, rubber, leather, paper and wood



Relationship of curing rate with the base material

The curing speed depends on the adhered base material. The following table suggests the curing time of Yuwang YT**1 adhering different base materials under the conditions of *3℃/*0% relative humidity. Curing time is defined as the time of sample shear strength reaching 0.1N/nm2.

Curing time, seconds:

Steel (degreasing)***5

Aluminum ***0

Neoprene ﹤5

Nitrile rubber ﹤5

ABS ***5

PVC     ***5

Polycarbonate ****0

Phenolic resin ***0

Wood (cork wood)﹤5

Wood (oak wood)*5 to *0

Wood (pine wood) *5 to *0

hardboard ﹤*0

fabric *0 to *0

leather *5 to *0

paper ﹤5



Relationship of curing rate with adhesion gap

Curing rate depends on the adhesion gap. If adhesion gap is smaller, curing rate will be more rapid. Increased adhesion gap will reduce the curing rate.



Relationship of curing rate with an accelerant

In case that curing is too slow due to too large adhesion gap, it is feasible to increase the curing rate by usingan accelerant on the surface of base material. However, such treatment will reduce the final strength of adhesion. Therefore, it is recommended to conduct testing for determining the actual adhesion effect.



Typical performances of adhesive base materials

Adhesive performance

Curing time of *@********************an>℃

Tensile shear strength.GB/T ********8     MPa ≥4.8



Curing time of *2h